See Through Beauty. Built for the Spotlight
Engineered for high-end anterior restorations, UT-ML offers a remarkable blend of translucency (49–53%) and natural gradient shading across 9 layers—no staining required. With 600–800 MPa flexural strength, it’s ideal for crowns, veneers, and inlays where beauty and precision matter most. Available in VITA 16 and Ivoclar B4 shades, UT-ML delivers consistent, lifelike results that turn smiles into statements.
|
Stage |
Temperature (°C) |
Heating/Cooling Rate (°C/min) |
Holding Time (°C/min) |
|
1 |
Room Temperature～100 |
3 |
— |
|
2 |
100～1000 |
6 |
— |
|
3 |
1000 |
— |
10 |
|
4 |
1000～1500 |
5 |
— |
|
5 |
1500 |
— |
120 |
|
6 |
1500～Room Temperature |
-15 |
— |
|
Density after sintering |
6.07±0.02g·cm⁻³ |
|
CTE(25-500℃) |
(10.5 ± 0.5) × 10⁻⁶ K⁻¹ |
|
Fracture toughness |
3.5–5.0 MPa·m¹ᐟ² |
|
Accelerated aging surface monoclinic phase content |
<5% |
|
Chemical solubility after sintering |
< 100 µg·cm⁻² |
|
Radioactivity |
< 0.1 Bq·g⁻¹ |
|
Sintering temperature |
1470-1500；Recommended 1500°C |
|
ZrO₂ + HfO₂ + Y₂O₃ |
≥99% |
|
Y₂O₃ |
8.0%-10.0% |
|
Al₂O₃ |
＜0.15% |
|
Other Oxides |
＜0.5% |